LNP™ STAT-KON™ RE008 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kGflsE_LNP-STAT-KON-RE008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RE008 is a compound based on Nylon 66 containing 40% Carbon Fiber. Characteristics of this grade include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound EMI-X RC-1008 Product reorder name: RE008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 33300 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 259 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield | 250 | % | ISO 527-2/5 |
| Break 3 | 1.3 | % | ASTM D638 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 25600 | MPa | ASTM D790 |
| -- 5 | 25000 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 390 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 7 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 256 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 255 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XWB-4520 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ASTALON™ S3600R | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| DSR TL-8080 | Dragon Special Resin (Xiamen) Co., Ltd. | PET | DSR |
| K-vinyl 60 Deg C Rating Insulation (85-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| POLIGOM G/35 | Crosspolimeri S.p.A. | EPDM | POLIGOM |