Epocast 1627-2
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kGaxsz_Epocast-1627-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 1627-2 epoxy syntactic is a filled, high-performance, structural core-reinforcing compound with an extremely low coefficient of thermal expansion, making the material suitable for use in fabricating and reinforcing composite structures. The epoxy syntactic is supplied ready to use (after thawing) as a gray-colored, frozen, 32- or 64-cubic inch (524 or 1,049 cm 3 ) patty which does not require any weighing or mixing. Epocast® 1627-2 epoxy syntactic is qualified to BMS 5-28, Type 27. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | ASTM D1622 |
| Shrinkage | 0.20 | % | ASTM D696 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Extrudability (25°C) | 1000 | g/min | ATM 5-28 |
| Weight Gain 1 | ASTM D543 | ||
| BMS 3-11, Type IV, Class I : 25°C | 0.40 | % | ASTM D543 |
| Distilled water : 25°C | 0.20 | % | ASTM D543 |
| MIL-H-5606 hydraulic fluid : 25°C | 0.40 | % | ASTM D543 |
| TT-3-735, Type III : 25°C | 0.10 | % | ASTM D543 |
| Work Life - after thaw (25°C) | 1.0 | day | ASTM D1338 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | ASTM D695 | ||
| -- 2 | 414 | MPa | ASTM D695 |
| -- 3 | 13100 | MPa | ASTM D695 |
| Compressive Strength | ASTM D695 | ||
| 25°C | 207 | MPa | ASTM D695 |
| 177°C | 24.1 | MPa | ASTM D695 |
| Shear Strength | ASTM D1002 | ||
| 25°C | 6.89 | MPa | ASTM D1002 |
| 163°C | 3.45 | MPa | ASTM D1002 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D3386 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| SUGGESTED CURE SCHEDULES:#1 - 1 hour at 350°F (177°C)#2 - 6 hours at 250°F (121°C)#3 - 4 days at 180°F (83°C)Each cure cycle must include 5-7°F (3-4°C) per minute heat rise from room temperature to cure temperature, holding at cure temperature for designated time, followed by 5-7°F (3-4°C) per minute heat reduction to 150°F (66°C) or below. Cure temperature refers to temperature of material as determined by thermocouple. |
| Note Message | |
|---|---|
| 1 . | on immersion - 24 hrs |
| 2 . | at 177°C |
| 3 . | at 25°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP ERTACETAL® C | Quadrant Engineering Plastic Products | Acetal (POM) Copolymer | Quadrant EPP |
| Boltaron 9815P | Boltaron Performance Products | PVC Alloy | Boltaron |
| GAPEX® RPP43EV01NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| LEXAN™ HFD4472 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LUVOCOM® 1/XCF/20 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |