Laticonther 75 GR/50
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kGQGyC_Laticonther-75-GR-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High thermal conductivity product based on Polybutylene Terephtalate (PBT). Graphite. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 1.0 | % | |
| Flow : 2.00 mm | 0.50 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.80 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| Thermal Conductivity | 10 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 25 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Wellamid® GF1685-WBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| UNISOFT ADHESION™ AD-40A-BK-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT ADHESION™ |
| Ultrason® E KR 4113 | BASF Corporation | PESU | Ultrason® E |
| Bapolene® 105F | Bamberger Polymers, Inc. | LDPE | Bapolene® |