Veroplas PA2002
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Veroplas |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kGGCy9_Veroplas-PA2002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Veroplas PA2002 is a polyamide 6 (nylon 6) product,. It can be processed by injection molding and is available in North America or Europe. The main characteristics are: impact modification. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 48.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 171 | °C | ASTM D1525 |
| Additional Information |
|---|
| Glow Wire Test, UNE 20-672-83: 1200°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.17 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1399 X 97649 D | RTP Company | PPS | RTP |
| STAR-THERM® W A N | EPIC Polymers | Nylon 66 | STAR-THERM® |
| Evermore PUR SA-2321HR | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| KOPA® KN3311BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LNP™ STAT-KON™ CD000I compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ STAT-KON™ |