TAROLON 2500 G3
| Category: | PC , Polycarbonate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kG5ccN_TAROLON-2500-G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate medium viscosity, 15% glass fiber reinforced. Available: all colors, UV stabilized (L), release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 to 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.080 | % | ASTM D570, ISO 62 |
| Saturation | 0.25 | % | ASTM D570 |
| Saturation, 23°C | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4600 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 80.0 | MPa | |
| Break | 80.0 | MPa | |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 125 | MPa | ISO 178 |
| -- 2 | 120 | MPa | ISO 178 |
| Yield | 125 | MPa | ASTM D790 |
| Break | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 10 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 142 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 4 | 130 | °C | IEC 60216 |
| Vicat Softening Temperature | 153 | °C | ISO 306/A50, ASTM D1525 5 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 3.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-1 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Break |
| 3 . | 6x4x50 mm |
| 4 . | 20000 hrs |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom X05041 | Spartech Polycom | PP, Unspecified | Spartech |
| Sylvin 9703-85 Red 6274 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MAGNUM™ 3616 | Trinseo | ABS | MAGNUM™ |
| Sylvin 83001-50 Red 6238 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Hifax TYC 1190P 3004 BLACK | LyondellBasell Industries | TPO (POE) | Hifax |