LNP™ THERMOTUF™ WF006N compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kFEOD6_LNP-THERMOTUF-WF006N-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
30% glass fiber reinforced, high metal bonding strength, high flow, for NMT application |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 14.0 | cm³/10min | |
| 275°C/5.0 kg | 26.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.12 | % | |
| Across Flow | 0.28 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7900 | MPa | ASTM D638 |
| -- | 8200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 120 | MPa | ISO 527-2/5 |
| Break 3 | 110 | MPa | ASTM D638 |
| Break | 120 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.7 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2/5 |
| Break 5 | 2.7 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6600 | MPa | ASTM D790 |
| -- 7 | 7400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 166 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 156 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 62 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 170 | J/m | ASTM D256 |
| -30°C 9 | 11 | kJ/m² | ISO 180/1A |
| 23°C 10 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 840 | J/m | ASTM D4812 |
| 23°C 11 | 52 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 175 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 158 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ASTM D1525 13 |
| -- | 157 | °C | ISO 306/B50 |
| CLTE | |||
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 1.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 1.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.1E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant | Internal Method | ||
| 1.10 GHz | 3.53 | ||
| 1.90 GHz | 3.54 | ||
| Dissipation Factor | Internal Method | ||
| 1.10 GHz | 0.012 | ||
| 1.90 GHz | 0.011 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 100 to 160 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E490 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| APEX® 3701-65NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Fainplast PVC FK 90/13 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| PERLER® N09H0000B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| OTECH TPE OTE7030 - A/V Jacket | OTECH Corporation | TPE | OTECH TPE |