Next Nylon 6 Industrial Series NXF-02WH
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Industrial Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kEkQoT_Next-Nylon-6-Industrial-Series-NXF-02WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Un Filled FR White compound Product Applications Connectvity -junction block, Terminal blocks, connectors etc Benefits Execellent mold ability with good stiffness & UL-94 V0 at 0.8mm thickness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.17 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.0 | -- | % | ASTM D955 |
| Transverse flow | 1.1 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.1 | -- | % | ASTM D570 |
| Saturation 1 | 5.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 70 | -- | ASTM D785 | |
| Class r | 85 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2900 | 1800 | MPa | ASTM D638 |
| Tensile Strength | 70.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | 20 | % | ASTM D638 |
| Flexural Modulus | 2750 | -- | MPa | ASTM D790 |
| Flexural Strength | 100 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 120 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | -- | °C | ASTM D648 |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2939-75 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Bergamid™ A70 G30 U NC284 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| FARALLOY® PP-130 | O'Neil Color and Compounding | PP, Unspecified | FARALLOY® |
| Deprene 251-60 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| CYCOLOY™ LG9000 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |