EL-Lene™ H2001WC
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kDrhtc_EL-Lene-H2001WC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EL-Lene H2001WC is a black bimodal high density polyethylene compound for jacketing in fiber optic and power cable applications. It contains well-dispersed carbon black of nominal particle size less than 20 nanometer to provide excellent weathering resistance and UV resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D1505 | ||
| -- 1 | 0.952 | g/cm³ | ASTM D1505 |
| -- 2 | 0.963 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.13 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Molded, F0) | > 10000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 24.0 | MPa | ASTM D638 |
| Fracture | 34.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 840 | % | ASTM D638 |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.56 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D1531 |
| Additional Information |
|---|
| Carbon Black Content, ASTM D1603:2.5% wtOxidation Induction time, ISO/TR10837, 200°C: > 70 min |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 95.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Melt Temperature | 190 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | Base Resin |
| 2 . | Compound |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rulon® W2 | Saint Gobain Performance Plastics | PTFE | Rulon® |
| Ravago Compounds HM-242 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| RheTech Polypropylene GC20P100-177UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Forprene® 6SD001A55 | SO.F.TER. SPA | TPV | Forprene® |
| Kepex® 3300VS | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |