HAIPLEN H30 G10 BA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kDG8zq_HAIPLEN-H30-G10-BA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer glass fiber reinforced 50% chemical coupled, very good mechanical properties. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.35 | % | |
| Across Flow | 0.40 to 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 165 | °C | ASTM D1525, ISO 306/A50 2 1 |
| -- | 140 | °C | ASTM D1525, ISO 306/B50 3 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9945T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| MOSTEN FC 110 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Moplen H500J | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Hostaform® LW15EWX | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Lumid® HI2152A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |