Polifor® L6 GF/50 NATURALE
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Polifor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kCacgX_Polifor-L6-GF-50-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer reinforced with 50% chemically coupled glass fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 94.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 9000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 1 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bio-Flex® F 2110 | FKuR Kunststoff GmbH | PLA | Bio-Flex® |
| LNP™ LUBRICOMP™ RFL26 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ JF004E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |
| Hostacom PPU X9067HS C12470 | LyondellBasell Industries | PP Copolymer | Hostacom |
| SABIC® LDPE 2502X0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |