OPNYL OP66GF60
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kBxElg_OPNYL-OP66GF60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 66 - Glass reinforced (60 %), high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.17 mm) | 0.10 to 0.35 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6800 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 220 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 17200 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 330 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 252 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer EVA 18-3 | Shanghai Potomer International Trade Co., Ltd. | EVA | Shanghai Potomer |
| Trovicel® 10 mm | Röchling Engineering Plastics SE & Co. KG | PVC, Flexible | Trovicel® |
| NORDEL™ IP 3722P EL | The Dow Chemical Company | EPDM | NORDEL™ |
| Hanwha Total PP TB81W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina BLACK PVC COMPUND 850-48/ 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |