Texalan® 2 Series 298A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Austin Novel Materials Co. Ltd. |
| Trademark: | Texalan® 2 Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kBWPOl_Texalan-2-Series-298A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Texalan® 2 Series 298A is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) material. It is available in Asia Pacific, Europe, or North America for blow molding, calendering, coextrusion, extrusion, film extrusion, or injection molding. Important attributes of Texalan® 2 Series 298A are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 to 1.24 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 95 to 101 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance | < 50.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% Strain | > 11.0 | MPa | |
| 300% Strain | > 24.0 | MPa | |
| Tensile Stress (Yield) | > 46.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | > 440 | % | ISO 37 |
| Tear Strength | > 130 | kN/m | ISO 34-1 |
| Compression Set (70°C) | < 50 | % | ISO 815 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ R340T | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| ELASTOSIL® R plus 4450/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| HiFill® PEEK 0145 B | Techmer Engineered Solutions | PEEK | HiFill® |
| LNP™ THERMOCOMP™ ZF0049 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ THERMOCOMP™ |
| Sylvin 8215-65FUV White 1545 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |