DOMAMID® 6G50H
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kBEA6h_DOMAMID-6G50H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, 50% glass fiber reinforced, heat stabilized, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 23°C, 72 hr | 0.40 to 0.60 | % | |
| Flow : 23°C, 72 hr | 0.10 to 0.20 | % | |
| Viscosity Number | 145 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 225 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 14500 | MPa | ISO 178 |
| Flexural Stress 3 | 325 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 95 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 95.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 90.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra TPU 95A Ether | ResMart | TPU-Polyether | ResMart Ultra |
| Vydyne® 67R NT0706 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| VECTRA® A725 | Celanese Corporation | LCP | VECTRA® |
| Epoxies, Ect. 20-1710 | Epoxies, Etc. | Silicone Gel | Epoxies, Ect. |
| Karina BLACK PVC COMPOUND -E 805D48/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |