SABIC® LLDPE 6318BE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAvYkH_SABIC-LLDPE-6318BE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 6318BE is a hexene linear low density polyethylene resin for cast film applications. The product has been specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Films produced from this grade exhibit good optical properties, toughness, puncture resistance and tear strength. The suffix E denotes European origin. Application SABIC® LLDPE 6318BE resin is typically used for pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required.The grade is also suggested for blending with ethylene/butene copolymer LLDPE and LDPE for improving strength. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Elastic Recovery - Cast Film (20.0 µm) | 56 | % | ASTM D5459 |
| Protrusion Puncture Resistance - Cast Film (20.0 µm) | 2.70 | J | ASTM D5748 |
| Retention Force - 60 sec (20.0 µm) 1 | 950 | g | |
| Stress Retention - Cast Film (20.0 µm) | 78 | % | ASTM D5459 |
| Ultimate Pre-stretch Level - Cast Film (20.0 µm) | 290 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Impact - Cast Film (20.0 µm) | 18.0 | J/cm | ISO 7765-2 |
| Peel Cling 2 | ASTM D5458 | ||
| 0% pre-stretch : 20.0 µm | 229.4 | g/2.5 cm | ASTM D5458 |
| 200% pre-stretch : 20.0 µm | 102.0 | g/2.5 cm | ASTM D5458 |
| Tear Strength - TD (20.0 µm) 3 | 246.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ISO 306/A |
| Melting Temperature (DSC) | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 90 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 1.8 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch line: melt temperature 270°C, chill roll temperature 20°C and line speed 450 m/min. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 - 300 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| 2 . | Cast Film |
| 3 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE LD2923F | Trademark Plastics Corporation | LDPE | Trademark PE |
| Nanjing Hongrui PBT T306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| GAPEX® RPP20EB92BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| LOXIM 100 00 V2 | LOXIM Industries Private Limited | PC | LOXIM |
| EnviroTPO 2010T20 | West Michigan Compounding | Polyolefin, Unspecified | EnviroTPO |