LUVOCOM® 16-0665 Datasheet,PARA,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®16-0665 is a polyacrylamide (PARA) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 16-0665 are: Conductivity High stiffness high strength Electrostatic protection Wear-resistant Typical application areas include: engineering/industrial accessories Electrical/electronic applications textile/fiber Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Additive	PTFE lubricant
Features	Conductivity Low friction coefficient Rigidity, high High strength Electrostatic discharge protection Good wear resistance Lubrication
Uses	Gear Textile applications Engineering accessories Switch Application in Automobile Field Business equipment Bearing
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.37	g/cm³	ISO 1183
Molding Shrinkage	0.10 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.30	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	17000	MPa	ISO 527-2
Tensile Stress (Break)	205	MPa	ISO 527-2
Tensile Strain (Yield)	1.8	%	ISO 527-2
Flexural Modulus	14000	MPa	ISO 178
Flexural Stress	285	MPa	ISO 178
Flexural Strain at Flexural Strength	2.6	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	195	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength
-30°C	37	kJ/m²	ISO 179/1fU
23°C	40	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	270	°C	ISO 75-2/A
Continuous Use Temperature	165	°C	UL 746B
CLTE - Flow	2.0E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.36	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+4	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
B	130	°C
Hot air dryer, A	100	°C
Drying Time
B	4.0 - 6.0	hr
Hot air dryer, A	6.0 - 8.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	260 - 300	°C
Middle Temperature	260 - 300	°C
Front Temperature	260 - 300	°C
Nozzle Temperature	250 - 290	°C
Processing (Melt) Temp	285	°C
Mold Temperature	110 - 140	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PARA , Polyarylamide
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kAOZ9N_LUVOCOM-16-0665.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Veroplas SERG1	PlastxWorld Inc.	ABS	Veroplas
Anjacom® 150-GF50	Almaak International GmbH	PC	Anjacom®
DOKI® PS 472	DIOKI d.d.	PS (HIPS)	DOKI®
Hostacom TSOP EM5 G23006	LyondellBasell Industries	PP Copolymer	Hostacom
Plaslube® AC-80/TF/20 NAT	Techmer Engineered Solutions	Acetal (POM) Copolymer	Plaslube®