Ultramid® B3WGM24 BK30564
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k6Ah5l_Ultramid-B3WGM24-BK30564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3WGM24 BK30564 is a 30% glass/mineral reinforced heat stabilized to high rigidity and high dimensional stability. Applications Typical applications include automobile engine covers, housings and automotive door handles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 205 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9300 | 4200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 120 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 10 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8400 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 7.0 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 50 | 45 | kJ/m² | |
| 23°C | 52 | 60 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 5.5 | 13 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| CLTE - Transverse | 3.6E-5 | 8.0E-5 | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SBF3748 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| ETILINAS MD20YW | POLYETHYLENE MALAYSIA SDN BHD | MDPE | ETILINAS |
| Lupol® TE5109 | LG Chem Ltd. | PP, Unspecified | Lupol® |
| Plaslube® PA6/6 M/TL7 HS L | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| NORYL GTX™ GTX985 resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |