perfluorence Tribocompound CoPEEK+PTFEcg
| Category: | PEEK+PTFE , Polyetheretherketone + PTFE |
| Manufacturer: | perfluorence GmbH |
| Trademark: | perfluorence Tribocompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k3F7Pn_perfluorence-Tribocompound-CoPEEK-PTFEcg.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The chemical compatibilization of polyetheretherketone (PEEK) and polytetrafluoroethylene (PTFE) will result in a semi-crystalline thermoplastic polymer compound with a homogeneous and stable processing morphology. The compound exhibits improved impact strength and excellent tribological properties. The thermal and chemical resistance corresponds to the properties of the PEEK matrix material. The granules can be processed under the processing conditions of the matrix material by extrusion or injection molding. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (380°C/5.0 kg) | 37 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | 78.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 5.0 | % | |
| Break | 9.0 | % | |
| Flexural Modulus | 3150 | MPa | ISO 178 |
| Flexural Stress | 123 | MPa | ISO 178 |
| Coefficient of Friction 1 | 0.18 | ISO 7148 | |
| Flexural Strain at Flexural Strength | 6.4 | % | ISO 178 |
| Wear Coefficient 2 | 2.10E-6 | mm³/(N·m) | ISO 7148 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 152 | °C | ISO 11357-2 |
| Melting Temperature | ISO 11357-3 | ||
| -- 3 | 325 | °C | |
| -- 4 | 340 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | IEC 60250 | ||
| 1 kHz | 3.10 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 kHz | 1.0E-3 | ||
| 1 MHz | 0.010 |
| Note Message | |
|---|---|
| 1 . | Block / ring test: FN = 100 N, v = 0,11 m/s, s = 10.000 m, Counterbody: Steel 100 Cr6, Rz = 3.2 microns, Conditions: technically dry |
| 2 . | Block / ring test: FN = 100 N, v = 0,11 m/s, s = 10.000 m, Counterbody: Steel 100 Cr6, Rz = 3.2 microns, Conditions: technically dry |
| 3 . | PTFE |
| 4 . | PEEK |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BITONER® TR-100 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Amilan® CM1061 | Toray Resin Company | Nylon 6 | Amilan® |
| INNOPOL® PP CS 1-5120 LH | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| OmniLon™ PA6 MF30 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |
| SABIC® PPcompound 7251U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |