Latene® AG7H K/30
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iwekbU_Latene-AG7H-K-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer (PPh) based compound. Fibres chemically coupled. Heat stabilised. Carbon fibre. Good thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.1 | % | |
| Flow : 2.00 mm | 0.20 to 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 15000 | MPa | |
| 60°C | 11000 | MPa | |
| 90°C | 7900 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 55.0 | MPa | |
| Break, 60°C | 35.0 | MPa | |
| Break, 90°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 0.90 | % | |
| Break, 60°C | 1.3 | % | |
| Break, 90°C | 2.3 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 160 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-6 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 MG 50 | RTP Company | PPA | RTP |
| Teflon® FEP 100 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| Moplen HP548R | LyondellBasell Industries | PP Homopolymer | Moplen |
| Karina CLEAR PVC COMPOUND -E 65/200-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9604-80 CLEAR 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |