RELENE® 52GB003

Category:	HDPE , High Density Polyethylene
Manufacturer:	Reliance Industries Limited
Trademark:	RELENE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ivDzlg_RELENE-52GB003.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
52GB003 is a Semi High Molecular Weight High Density Polyethylene blow moulding grade with high stiffness and impact strength and good ESCR. It possesses medium molecular weight distribution, very good swell and easy processability. 52GB003 can readily be processed on most HDPE blow moulding machines.

General Information
Features	Food Contact Acceptable Good Processability High ESCR (Stress Crack Resist.) High Impact Resistance High Molecular Weight High Stiffness Med.-Wide Molecular Weight Distrib.
Uses	Blow Molding Applications Containers Liners Sheet
Agency Ratings	FDA 21 CFR 177.1520 IS 10141-1982 IS 10146-1982
Processing Method	Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	0.952	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR)			ASTM D1238
190°C/21.6 kg	8.5	g/10 min
190°C/5.0 kg	0.45	g/10 min

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield, Compression Molded)	29.0	MPa	ASTM D638
Tensile Elongation (Yield, Compression Molded)	11	%	ASTM D638
Flexural Modulus (Compression Molded)	1000	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	No Break		ASTM D256

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	125	°C	ASTM D1525

Resin Grade	Manufacturer	Category	Trademark
AFLAS® 100H	Asahi Glass Co., Ltd.	Fluorelastomer	AFLAS®
ELASTOSIL® FLR 3900/40 A/B	Wacker Chemie AG	Silicone	ELASTOSIL® FLR
Geon™ Vinyl Rigid Extrusion L0189	PolyOne Corporation	PVC, Rigid	Geon™ Vinyl Rigid Extrusion
Kingfa AIP-2015	Kingfa	PP, Unspecified	Kingfa
Karina CLEAR PVC COMPOUND -E 70/217-D-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina