Generic PVC, Unspecified
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iuoCNU_Generic-PVC-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PVC, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 - 1.50 | g/cm³ | ASTM D792 |
| 23°C | 1.14 - 1.56 | g/cm³ | ISO 1183 |
| Apparent Density | |||
| -- | 0.23 - 0.63 | g/cm³ | ASTM D1895 |
| -- | 0.55 - 0.77 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 6.2 - 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 4.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 - 0.16 | % | ASTM D570 |
| K-Value (23°C) | 56.5 - 80.3 | ISO 1628-2 | |
| Viscosity Number (Reduced Viscosity) (23°C) | 83.1 - 161.4 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 12 - 108 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 59 - 97 | ASTM D2240 | |
| 23°C | 48 - 97 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1.79 - 87.5 | MPa | ASTM D638 |
| -- | 2960 | MPa | ISO 527-2 1 |
| Tensile Strength | |||
| Yield, 23°C | 7.96 - 42.8 | MPa | ASTM D638 |
| Yield, 23°C | 33.0 - 62.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 5.52 - 32.1 | MPa | ASTM D638 |
| Fracture, 23°C | 4.00 - 20.8 | MPa | ISO 527-2 |
| 23°C | 4.48 - 21.3 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 290 - 460 | % | ASTM D638 |
| Fracture, 23°C | 180 - 470 | % | ASTM D638 |
| Fracture, 23°C | 200 - 410 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1890 - 3030 | MPa | ASTM D790 |
| 23°C | 1890 - 2870 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 68.0 - 81.0 | MPa | ASTM D790 |
| 23°C | 68.4 - 92.0 | MPa | ISO 178 |
| Yield, 23°C | 55.4 - 94.5 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - MD (Yield) | 49.6 - 60.8 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break) | 100 - 120 | % | ASTM D882 |
| Water Vapor Transmission | 2.7 - 3.9 | g/m²/24 hr | ASTM E96 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% strain, 23°C | 2.85 - 17.4 | MPa | ASTM D412 |
| 100% strain, 23°C | 2.09 - 10.1 | MPa | ISO 37 |
| Tensile Strength (Yield, 23°C) | 7.83 - 23.6 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 220 - 390 | % | ASTM D412 |
| Tear Strength | |||
| 23°C | 23.6 - 106 | kN/m | ASTM D624 |
| 23°C | 26 - 72 | kN/m | ISO 34-1 |
| Compression Set | 47 - 48 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 11 - 25 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 21 - 1200 | J/m | ASTM D256 |
| 23°C | 2.5 - 18 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 7.16 - 65.8 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 11 - 22 | kJ/m² | ISO 180 |
| Drop Impact Resistance (23°C) | 63.1 - 267 | J/cm | ASTM D4226 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Ultimate Elongation in Air | |||
| 23°C | -5.5 - 8.4 | % | ASTM D573 |
| 23°C | -9.9 - 21 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 95.0 - 103 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 - 73.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.6 - 95.8 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 72.2 - 94.7 | °C | ASTM D648 |
| Continuous Use Temperature | 59.7 - 105 | °C | ASTM D794 |
| Brittleness Temperature | -50.1 - -4.45 | °C | ASTM D746 |
| Vicat Softening Temperature | |||
| -- | 76.7 - 85.0 | °C | ASTM D1525 |
| -- | 65.0 - 104 | °C | ISO 306 |
| 50°C/h, B (50N) | 78.8 | °C | ISO 306 2 |
| Melting Temperature | 159 - 185 | °C | |
| CLTE - Flow | 6.3E-5 - 7.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 1.0 - 1.5E+14 | ohms·cm | ASTM D257 |
| 23°C | 4.0E+12 - 1.8E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 13 - 40 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 2.83 - 3.70 | ASTM D150 | |
| 23°C | 2.75 - 3.40 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.012 - 0.025 | ASTM D150 | |
| 23°C | 0.012 - 0.019 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 4.3 - 6.4 | mm/min | ISO 3795 |
| Oxygen Index | |||
| -- | 20 - 31 | % | ASTM D2863 |
| -- | 24 - 41 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 88.8 - 90.1 | % | ASTM D1003 |
| Haze | 1.5 - 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 - 170 | °C | |
| Front Temperature | 170 - 175 | °C | |
| Processing (Melt) Temp | 165 - 188 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PVC, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 148 - 165 | °C | |
| Cylinder Zone 1 Temp. | 143 - 166 | °C | |
| Cylinder Zone 2 Temp. | 143 - 176 | °C | |
| Cylinder Zone 3 Temp. | 149 - 183 | °C | |
| Cylinder Zone 4 Temp. | 140 - 189 | °C | |
| Cylinder Zone 5 Temp. | 154 - 183 | °C | |
| Adapter Temperature | 154 - 177 | °C | |
| Melt Temperature | 163 - 188 | °C | |
| Die Temperature | 153 - 191 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PVC, UnspecifiedThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIZ4505W | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Vipel® F010-TBN-28 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Wanthane® WHT-1685AB | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| CP PRYME® Polycarbonate PC300HFR | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| ExxonMobil™ LDPE LD 313.NF | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |