FRIANYL® A3 GF07 V2XI
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | FRIANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | itbN3R_FRIANYL-A3-GF07-V2XI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRIANYL® A3 GF07 V2XI is a Polyamide 66 (Nylon 66) compound, 7% glass fiber reinforced, flame retardant with halogens, free from antimony trioxide, PBB and PBDE, UL listed V2. This compound is intended for injection molding. FRIANYL® A3 GF07 V2XI is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.90 | % | |
| Flow : 23°C | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.2 | % | |
| Saturation, 23°C | 6.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3900 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.5 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | 35 | kJ/m² | |
| 30°C | 28 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 120 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 400 | V | IEC 60112 |
| Needle Flame Test | IEC 60695-11-5 | ||
| 1.00 mm | Pass | ||
| 2.00 mm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-1 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 850 | °C | |
| 3.20 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 875 | °C | |
| 3.20 mm | 900 | °C | |
| Oxygen Index | 34 | % | ISO 4589-2 |
| Flammability 3 | SE | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| 3 . | 355x100x1mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4700 TFE 10 | RTP Company | PTT | RTP |
| TOPAS® 6013EC-01 | Polyplastics Co., Ltd. | COC | TOPAS® |
| Vydyne® R533H NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| HiFill® PET GF20 UV BK | Techmer Engineered Solutions | PET | HiFill® |
| KOCETAL® TF304 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |