TRIBOCOMP® PPS GF30 TS0
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | inyEEc_TRIBOCOMP-PPS-GF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRIBOCOMP®PPS GF30 TS0 is a polyphenylene sulfide (PPS) product, which contains fillers of 15% ptfe fiber and 30% glass fiber reinforcement. It is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.020 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 12100 | MPa | ISO 527-2 |
| 90°C | 9600 | MPa | ISO 527-2 |
| 120°C | 4800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 150 | MPa | ISO 527-2 |
| Fracture, 90°C | 110 | MPa | ISO 527-2 |
| Fracture, 120°C | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 210 | MPa | ISO 178 |
| Coefficient of Friction 1 | ASTM D3702 | ||
| Dynamic | 0.19 | ASTM D3702 | |
| Static | 0.17 | ASTM D3702 | |
| Wear Factor (23°C) | 90.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 275 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 260 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.31 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spectar™ UV Copolyester | Eastman Chemical Company | Copolyester | Spectar™ |
| ADDINYL PMD 20117 | ADDIPLAST | Nylon, Unspecified | ADDINYL |
| Bayflex® XGT-2 | Covestro - PUR | PUR-MDI | Bayflex® |
| Elastron® G P.G401.A45.701 | Elastron USA, Inc. | SEBS | Elastron® G |
| HiFill® PC/ABS FR 6218 | Techmer Engineered Solutions | PC+ABS | HiFill® |