DESLON™ 6 DSC104GM
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | in3iAs_DESLON-6-DSC104GM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC104GM is one of the brands which made by Polyamide6 that filled Glass Fiber & Mineral Filler 40%. It provides good mechanical property and good heat resistance property. Applications: DESLON™ DSC104GM is one of the most-used for surface appearance, good mechanical property and heat resistance goods due to excellent fluidity, such as Roof Rack, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 98.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 7850 | MPa | ASTM D790 |
| Flexural Strength | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 140 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 255 - 270 | °C | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Speed: 30 to 60%Pressure 1st: 30 to 70%Pressure 2nd: 30 to 70Holding Pressure: 10 to 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moldex® QS986A/M151 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| InnoTuf® TP-4055 | Innovative Polymers, Inc. | TSU | InnoTuf® |
| Lupoy® GN5001RFP | LG Chem Ltd. | PC+ABS | Lupoy® |
| Osterlene® HB0554 | Osterman & Company | HDPE | Osterlene® |
| Sylvin 9940-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |