LAMIGAMID® 320
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | imlEOt_LAMIGAMID-320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 2.2 | -- | % | ISO 62 |
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 175 | 150 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3800 | 3000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 100 | 80.0 | MPa | ISO 527-2 |
| Fracture | 150 | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 15 | -- | % | ISO 527-2 |
| Flexural Modulus | 3700 | 2800 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | |||
| 20% strain | 108 | -- | MPa | ISO 604 |
| 10% strain | 79.0 | -- | MPa | ISO 604 |
| 5% strain | 56.0 | -- | MPa | ISO 604 |
| Coefficient of Friction | ASTM D1894 | |||
| With steel-dynamic | 0.040 | 0.080 | ASTM D1894 | |
| With steel-static | 0.35 | -- | ASTM D1894 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | > 2.5 | > 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | No Break | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 120 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| CLTE - Flow (20 to 100°C) | 7.0E-5 - 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1670 | -- | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.25 | -- | W/m/K | ISO 8302 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Dielectric Strength | 50 | 20 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.70 | -- | IEC 60250 | |
| Dissipation Factor | 0.030 | -- | IEC 60250 |
| Additional Information |
|---|
| 干燥 Creep Rate Stress, DIN 53444, 1% Elongation: >12 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >18 N/mm²Friction Wear: 0.10 µm/KmPenetration Resistance, DIN 53482: 1E15 ohm-cmCreepage/leakage Resistance: KA3cThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: -40°C |
| 调节后的 Creep Rate Stress, DIN 53444, 1% Elongation: >6 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >10 N/mm²Friction Wear: 0.10 µm/KmPenetration Resistance, DIN 53482: 1E12 ohm-cmCreepage/leakage Resistance: KA3bThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: 120°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP461C | Southern Polymer, Inc. | PP Random Copolymer | PRIMALENE |
| Tectron H2270 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Staramide AG10K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Latigray 52/11-01 CX/45 | LATI S.p.A. | PP Homopolymer | Latigray |
| LubriOne™ AT-000/18T-2S BLK | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |