NYLAFORCE® B 60
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | NYLAFORCE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | imb62n_NYLAFORCE-B-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| produced by feed up-process, polyamide 6 + 60% glass fibres, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.70 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.10 to 0.40 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C 2 | -- | 14000 | MPa | |
| 23°C | 21000 | -- | MPa | |
| 80°C | 9800 | -- | MPa | |
| 120°C | 9600 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| 23°C 3 | -- | 185 | MPa | |
| 23°C | 265 | -- | MPa | |
| 80°C | 145 | -- | MPa | |
| 120°C | 110 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, 23°C 4 | -- | 4.5 | % | |
| Break, 23°C | 2.9 | -- | % | |
| Break, 80°C | 6.4 | -- | % | |
| Break, 120°C | 5.4 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 19 | -- | kJ/m² | |
| 23°C | -- | 29 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | 95 | -- | kJ/m² | |
| 23°C 5 | -- | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 6 | 221 | -- | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 60mm x 60mm x 2mm |
| 2 . | Tested accordiong to ISO 527/ISO 1110 |
| 3 . | Tested accordiong to ISO 527/ISO 1110 |
| 4 . | Tested accordiong to ISO 527/ISO 1110 |
| 5 . | Tested accordiong to ISO 179/ISO 1110 |
| 6 . | 10K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 505G | Marco Polo International, Inc. | HDPE Copolymer | MARPOL® |
| TABOREN PH 92 H 15 | SILON s.ro | PP Homopolymer | TABOREN |
| Toyolac® ASG-30 | Toray Resin Company | SAN | Toyolac® |
| Aaron AVPE LD 300-1 | Aaron Industries Corp. | LDPE | Aaron |
| ICORENE® N4425 | ICO Polymers EMEA, A Division of A. Schulman | PP Homopolymer | ICORENE® |