RTP 1107 TFE 10
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ilwB9g_RTP-1107-TFE-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. The coefficient of friction was tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. This material offers an excellent balance of strength, heat resistance and toughness in a wear resistant composite. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 221 | MPa | ASTM D790 |
| Compressive Strength | 172 | MPa | ASTM D695 |
| Coefficient of Friction (With Metal-Dynamic) | 0.15 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 232 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 227 | °C | ASTM D648 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.30 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, Linear-Flow, ASTM D955, 6.35mm: 2mm/m. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 260 - 299 | °C | |
| Middle Temperature | 260 - 299 | °C | |
| Front Temperature | 260 - 299 | °C | |
| Mold Temperature | 82.2 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Screw Speed | 60 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-2260N NAT | Teknor Apex Company | TPE | Sarlink® TPE |
| VESTOLIT® P 1415 K 80 Ultra | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| WELLAMID Nylon 6000 GV 30 HW | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Karina WHITE PVC COMPOUND 854-10/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECACOMP® PK TRM PVX black 4180 | Ensinger GmbH | PK | TECACOMP® |