TECHNYL® A 225F NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | il3Fgg_TECHNYL-A-225F-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL ® A 225F Natural is an unreinforced polyamide 66, medium viscosity, for injection moulding, with a special crystallizing agent, for very fast cycles. It is available in natural color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.8 | -- | % | |
| Flow | 1.5 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.1 | -- | % | |
| Saturation, 23°C | 1.1 | -- | % | |
| Molding Shrinkage Isotropy | 0.830 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 2000 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 85.0 | 55.0 | MPa | |
| Break | 70.0 | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 5.0 | 25 | % | |
| Break | 20 | 100 | % | |
| Flexural Modulus | 3150 | 1400 | MPa | ISO 178 |
| Flexural Stress | 125 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 5.0 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 6.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 4.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 2.90 | 3.20 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.380 mm | V-2 | -- | ||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DIALAC® S411A | UMG ABS, Ltd. | ASA | DIALAC® |
| Hanwha Total PP FH51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| MAJORIS FT103C | AD majoris | PP, Unspecified | MAJORIS |
| PARAPET HR-F | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |
| Plexiglas® Frosted V825-68177 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |