LubriOne™ PS-30GF/2S Natural
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ikdCsK_LubriOne-PS-30GF-2S-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.40 | % | |
| Across Flow | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8620 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 100 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 6690 | MPa | ASTM D790 |
| Flexural Strength 5 | 165 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.14 | ||
| vs. Steel - Static | 0.24 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 75 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 218 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 197 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRESEAL® TPE 6070 | Premix Oy | TPE | PRESEAL® |
| AKROMID® B3 F0 natural (1812) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| POCAN® B 4235 Z 000000 | LANXESS Corporation | PBT | POCAN® |
| Nylux 66G33H | KMI Group, Inc. | Nylon 66 | Nylux |
| Moplen HP500D | LyondellBasell Industries | PP Homopolymer | Moplen |