Stanyl® ForTii™ LED LX
| Category: | Nylon 4T , Polyamide 4T |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® ForTii™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ik0aKr_Stanyl-ForTii-LED-LX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stanyl® ForTii™ LED LX is a Polyamide 4T (Nylon 4T) material filled with glass fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of Stanyl® ForTii™ LED LX: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.60 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 230 | °C | ISO 75-2/A |
| Melting Temperature 1 | 325 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 320 to 330 | °C | |
| Middle Temperature | 325 to 335 | °C | |
| Front Temperature | 330 to 335 | °C | |
| Nozzle Temperature | 330 to 335 | °C | |
| Processing (Melt) Temp | 330 to 340 | °C | |
| Mold Temperature | 100 to 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 to 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL SB802 | AD majoris | Nylon 6 | VENYL |
| AlphaSeal™ 04-073 P MODIFIED | AlphaGary | TPE | AlphaSeal™ |
| BMC 501 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Plaslube® PC / ABS 720 BK | Techmer Engineered Solutions | PC+ABS | Plaslube® |
| AIE PP 8010HMS-TFHI | Asia International Enterprise (Hong Kong) Limited | PP, Unspecified | AIE PP |