DIAMALOY ASAPC 6040 is an Acrylonitrile Styrene Acrylate + PC (ASA+PC) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(265°C/5.0 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 48.7 | MPa | ASTM D638 |
| Flexural Modulus 3 | 2020 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 590 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 87.8 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 93.9 | °C | |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | Method I (3 point load), 1.3 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XENOY™ 1760 resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | XENOY™ |
| Nipol® LX433C | Zeon Corporation | Latex | Nipol® |
| DINALON® A1S25 G35 (Glass) | Grupo Repol | Nylon 66 | DINALON® |
| MAJORIS FN050X | AD majoris | PP, Unspecified | MAJORIS |
| POLYelast TPE HJ-75 UV1 | Polykemi AB | PP+EPDM | POLYelast |