RTP 300 SI 1
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | igiTau_RTP-300-SI-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2280 | MPa | ASTM D638 |
| Tensile Strength | 64.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Coefficient of Friction (With Metal-Dynamic) | 0.28 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 7mil/in.Wear Factor, K, ASTM D-3702: 250E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D-3702: 0.28The wear factor and dynamic coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 288 - 343 | °C | |
| Middle Temperature | 288 - 343 | °C | |
| Front Temperature | 288 - 343 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 135 | Salflex Polymers Ltd. | TPO (POE) | Salflex |
| NEFTEKHIM PP 7648H | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Boltaron 3042 TruPrint | Boltaron Performance Products | PVC, Rigid | Boltaron |
| Hyundai EP PA6 LS440 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Innoprene 1450N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |