NatureFlex™ NE30 (19µ)
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | NatureFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ig6Btk_NatureFlex-NE30-19-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NatureFlex™ NE30 (19µ) is a Regenerated Cellulose product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Film. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 1(vs. Itself - Dynamic) | 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 19 µm | > 3000 | MPa | |
| 1% Secant, TD : 19 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 19 µm | 125 | MPa | |
| TD : Yield, 19 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 19 µm | 22 | % | |
| TD : Break, 19 µm | 70 | % | |
| Seal Strength 2 | 0.16 | N/mm | Internal Method |
| Seal Initiation Temperature (19 µm) | 80.0 to 200 | °C | Internal Method |
| Oxygen Transmission Rate (Wet) (23°C, 19 µm, 0.0% RH) | 3.00 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission | |||
| -- 3 | 15 | g/m²/24 hr | DIN 53122 |
| -- 4 | 15 | g/m²/24 hr | BS 3177 |
| -- 5 | 30 | g/m²/24 hr | ASTM E96 |
| Film Gauge | 19.4 | µm | Internal Method |
| Yield (19.4 µm) | 35.7 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 19.4 µm) | 90 | ASTM D2457 | |
| Haze 6(19.4 µm) | 6.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Thickness: 19.4µ |
| 2 . | Thickness: 19.4µ |
| 3 . | 23°C, 85%RH, thickness: 19.4µ |
| 4 . | 25°C, 75%RH, thickness: 19.4µ |
| 5 . | 38°C, 90%RH, thickness: 19.4µ |
| 6 . | 2.5° wide angle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP731 9920 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| Grilamid® L 16 GM nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LUVOCOM® 19-8942 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| SD POLYCA™ LR8031V | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| TOTAL Polyethylene Lumicene® M 3421 UV black | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |