Ebalta AH 140 / TC 90-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ig3bTE_Ebalta-AH-140-TC-90-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta AH 140 is a very thin liquid two-component-epoxy resin with high values of strength and high heat resistance. Due to its very good impregnating and wetting properties it is suitable as laminating resin for high-strength components with fabrics of glass -or carbon fiber. Especially for thin laminates, a post-curing of 16 hours at 80°C, after curing at room temperature, is essential in order to guarantee a complete curing. Otherwise the non post-cured laminate will be brittle and the adhesion of the layers with each other will not be sufficient. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 84 to 90 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2600 to 3200 | MPa | ISO 178 |
| Flexural Stress | 115 to 135 | MPa | ISO 178 |
| Compressive Stress | 105 to 125 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 30 to 46 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 107 to 113 | °C | ISO 75-2/B |
| Glass Transition Temperature | 114 | °C | TMA |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 32 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time | |||
| 60°C | 4.0 to 6.0 | hr | |
| 80°C | 5.0 to 6.0 | hr | |
| 120°C | 4.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.10 to 1.14 | g/cm³ | |
| Viscosity (25°C) | 0.35 to 0.50 | Pa·s | |
| Curing Time (20°C) | 48 to 72 | hr | |
| Pot Life 1(20°C) | 90 to 110 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TPSF-G30 | Polymer Resources Ltd. | PBT | PRL |
| RELENE® B 31101 | Reliance Industries Limited | HDPE | RELENE® |
| Chemlon® 100 HU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| INEOS PP 101-SA09 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| PSM® HL-303 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |