XANTAR® C CM 406 U
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ielOor_XANTAR-C-CM-406-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vicat 120°C, UV Stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 24.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/4A | ||
| -40°C | 35 | kJ/m² | |
| -20°C | 55 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 675 | °C | |
| 3.00 mm | 675 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 700 | °C | |
| 3.00 mm | 700 | °C | |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity of Melt | 0.23 | W/m/K |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Ject® 1100V-20 | Premix, Inc. | TS, Unspecified | Premi-Ject® |
| RELENE® O19010 | Reliance Industries Limited | LLDPE | RELENE® |
| Michilene F8100GC30-01 | API Polymers, Inc. | PP Homopolymer | Michilene |
| DI-COAT R-4721LV/7 | Hapco Inc. | TP, Unspecified | DI-COAT |
| LEXAN™ BY2710X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |