SABIC® PPcompound 8250U
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ieYxNm_SABICPPcompound8250U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8250U is a mineral filled modified polypropylene for use in Automotive exterior unpainted applications. This material has been designed to combine good mechanical performance in combination with excellent esthetical performance. SABIC® PPcompound 8250U is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A | ||
| Yield, injection molding | 16.0 | MPa | ISO 527-2/1A |
| Fracture, injection molding | 12.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, Injection Molded) | 100 | % | ISO 527-2/1A |
| Flexural Modulus (Injection Molded) | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/4A | ||
| -20°C, injection molding | 10 | kJ/m² | ISO 180/4A |
| 0°C, injection molding | 25 | kJ/m² | ISO 180/4A |
| 23°C, injection molding | No Break | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PP P302 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Cheng Yu FRCV200 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| E-RIALGLASS C 07 S 30 G | RIALTI Srl | PP Copolymer | E-RIALGLASS |
| LUVOCOM® PEEK CLASSIX 7918 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Polimid B EM1 | Poliblend S.p.a. | Nylon 6 | Polimid B |