ASTAMID™ MN-3020X7
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iagWV1_ASTAMID-MN-3020X7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MN-3020X7 is a heat and UV stabilized Polyamide 12 based compound used for termite resistant jackets for communication cables. The hard surface of the Nylon 12 resists attack from termites in areas where they may be a problem. This material conforms to the requirements of the AS1049 standard. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 200 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1500 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 59.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | 4.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (3.20 mm) | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 92.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 47.0 | °C | |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | > 2.0 | hr | |
| Cylinder Zone 1 Temp. | 170 to 180 | °C | |
| Cylinder Zone 2 Temp. | 180 to 185 | °C | |
| Cylinder Zone 3 Temp. | 185 to 190 | °C | |
| Cylinder Zone 4 Temp. | 190 to 195 | °C | |
| Melt Temperature | 170 to 180 | °C | |
| Die Temperature | 160 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP3B40 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Stylac™ IM30 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Amilan® CM3006G-30 | Toray Resin Company | Nylon 66 | Amilan® |
| DESOX™ DSC490C | DESCO Co., Ltd. | PC+PBT | DESOX™ |
| LNP™ LUBRICOMP™ KL002L compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |