LEXAN™ FST3002 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iXYmKz_LEXAN-FST3002-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN FST3002 resin is a halogen-free flame retardant PC Copolymer Resin with MVR of 8, suitable for injection molding. This resin is EN45545 R6 HL2 compliant and an ideal candidate for train interior applications (category R6). Available in opaque colors |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2450 | MPa | ASTM D638 |
| -- | 2450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 75.0 | MPa | ASTM D638 |
| Yield | 74.0 | MPa | ISO 527-2/50 |
| Break 3 | 63.0 | MPa | ASTM D638 |
| Break | 59.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | > 50 | % | ASTM D638 |
| Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2600 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 107 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 9 | 7.0 | kJ/m² | |
| 23°C 10 | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C 11 | No Break | ||
| 23°C 12 | No Break | ||
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 23°C | 70 | J/m | ASTM D256 |
| -30°C 13 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 14 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C 15 | No Break | ||
| 23°C 16 | No Break | ||
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 70.0 | J | ASTM D3763 |
| -- | 130 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 121 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 17 | 125 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 18 | 111 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 19 |
| -- | 141 | °C | ISO 306/A120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.2E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fire Safety Hazard Level - Requirement set R6 | HL2 | EN 45545-2 | |
| Heat Release, MAHRE - 50 kW/m² (3.00 mm) | < 90.0 | kW/m² | ISO 5660-1 |
| Smoke Density | ISO 5659-2 | ||
| DS-4, 50 kW/m² : 3.00 mm | < 300 | ||
| VOF4, 50 kW/m² : 3.00 mm | < 600 | ||
| Smoke Toxicity - CITG (8 min), 50 kW/m² (3.00 mm) | < 0.900 | ISO 5659-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 |
| 15 . | 80*10*3 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 mm |
| 18 . | 80*10*4 mm |
| 19 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTADUR PET | Röchling Sustaplast SE & Co. KG | PET | SUSTADUR |
| WPP PP VB-511 | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| DENILUB B 00U 0Mo | Vamp Tech | PBT | DENILUB |
| Fiberfil® J-60/30/E5 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Geon™ Vinyl Flexible MD403KB | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |