LNP™ LUBRICOMP™ RFL26 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iX9wWO_LNP-LUBRICOMP-RFL26-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RFL26 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4026 Product reorder name: RFL26 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 185 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638 |
| Flexural Strength | |||
| -- | 276 | MPa | ASTM D790 |
| -- | 262 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.61 | ASTM D3702 Modified | |
| Wear Factor - Washer | 6.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | 4.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (-40 to 40°C) | 3.0E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADENE ONOEG | A.D. Compound spa | PP Copolymer | ADENE |
| Colorite 66 Series 6066 | Colorite Polymers | PVC, Unspecified | Colorite 66 Series |
| ExxonMobil™ PP7035E4 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Huafon HF-1075AP | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Sylvin 9048-97 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |