Talcoprene® 1522SMT NERO
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Talcoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iWEly3_Talcoprene-1522SMT-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, 21% mineral filled, high heat resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 1.3 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2250 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 3.3 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Phenolic FM 7700P | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Sumitomo Silicone SI 9002J-1 | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| UNIPA® im | Nytef Plastics, Ltd. | Nylon 66 | UNIPA® |
| DuraSurf™ SW 2001 | Crown Plastics | UHMWPE | DuraSurf™ |
| Jampilen RP348U | Jam Polypropylene Company | PP Random Copolymer | Jampilen |