Ultrathene® UE672006
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Ultrathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iVAImb_Ultrathene-UE672006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultrathene UE672 is a series of EVA copolymer resins with good toughness, flexibility and clarity. Typical applications include laminating and heavy duty films as well as injection and blow molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 13.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 90.3 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 91.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 6.62 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 5.52 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 30.5 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 29.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 18 | % | ASTM D882 |
| TD : Yield, 38 µm, blown film | 16 | % | ASTM D882 |
| MD : Broken, 38 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 600 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 570 | g | ASTM D4272 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 92 | g | ASTM D1922 |
| TD : 38 µm, blown film | 130 | g | ASTM D1922 |
| Oxygen Transmission Rate (23°C, 38 µm, blown film) | 8900 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 38 µm, blown film) | 85 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 |
| Melting Temperature | 94.4 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm, Blown Film) | 88 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 1.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| NAS 1(38.1 µm) | 78.0 | ASTM D1746 | |
| Physical properties measured on 1.5 mil film produced on a 2" BGE extruder w/4" Davis-Standard die, 25 mil die gap, 420 °F melt temperature @50 lb/hr, 2:1 BUR. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 232 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-8185 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |
| AKROMID® S3 GF 30 4 black (3429) | AKRO-PLASTIC GmbH | Nylon 610 | AKROMID® |
| Hanwha Total PP BI750 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Hostacom ERC 204N D G91428 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LEXAN™ 945A resin | SABIC Innovative Plastics | PC | LEXAN™ |