EMERGE™ PC/ABS 7770
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iV8oYH_EMERGE-PC-ABS-7770.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/ABS 7770 advanced resin is a high flow, ignition-resistant PC/ABS blend that contains no chlorinated or brominated additives. It combines elevated heat performance with the excellent processing characteristics associated with other EMERGE™ PC/ABS Advanced resins, meeting the market trend in Flat TV housing for higher heat, higher flow materials. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/3.8 kg | 20 | g/10 min | |
| 260°C/5.0 kg | 70 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm, Injection Molded) | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm, Injection Molded | 70.0 | MPa | |
| Break, 4.00 mm, Injection Molded | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm, Injection Molded | 5.0 | % | |
| Break, 4.00 mm, Injection Molded | 25 | % | |
| Flexural Modulus 1(4.00 mm, Injection Molded) | 2900 | MPa | ISO 178 |
| Flexural Stress 2(4.00 mm, Injection Molded) | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength 3(23°C, Injection Molded) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 88.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ISO 306/A120 |
| -- | 105 | °C | ISO 306/B50 |
| Ball Indentation Temperature | 98.0 | °C | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 4(1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index 5 | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 3.00 mm | 850 | °C | |
| Glow Wire Ignition Temperature 6 | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 775 | °C | |
| 3.00 mm | 775 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4 mm |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800.5 | RTP Company | Acetal (POM) Copolymer | RTP |
| METALCAP PPC370B60 | Polyram Ram-On Industries | PP Copolymer | METALCAP |
| Lifoflex® GA 1030 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| Sylvin 8260-95FR Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Infino LS-1159S | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |