Riblene® FH 20
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iV21NP_Riblene-FH-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FH 20 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FH 20 is characterised by a good balance between processability and mechanical properties. Films manufactured by Riblene FH 20 are easily heat shrinkable and have good optical and mechanical properties. Main Application Riblene FH 20 is recommended for general packaging film and for diapers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 30 to 100 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 40 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 40 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 22.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm, Blown Film | 350 | % | |
| TD : Break, 40 µm, Blown Film | 600 | % | |
| Dart Drop Impact 1(40 µm, Blown Film) | 140 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 40.0 µm | 80.0 | kN/m | |
| TD : 40.0 µm | 55.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 71 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 6.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551800-100 (3.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| TEREZ PA 6.10 7500 GF 30 ECO | TER HELL PLASTIC GMBH | Nylon 610 | TEREZ PA 6.10 |
| AMTOPP BA15 | Inteplast Group | PP, Unspecified | AMTOPP |
| KumhoSunny PPO HSP8370 | Shanghai KumhoSunny Plastics Co., Ltd. | PPE+PS | KumhoSunny PPO |
| Karina GRAY COLOR CONCENTRATE 18/ 89-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |