TECHNYL® A 218W V15 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iUxUzV_TECHNYL-A-218W-V15-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, reinforced with 15% of glass fibre, for injection moulding, heat stabilized, with improved hydrolysis resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.1 | % | |
| Flow | 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.730 | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6070 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | 5270 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 5.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | °C | ISO 75-2/Af |
| Melting Temperature | 263 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 680K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| Moplen HP550J | LyondellBasell Industries | PP Homopolymer | Moplen |
| Bayblend® FR3010 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Grivory® HT2C-3X LF black 9833 | EMS-GRIVORY | Nylon 6T/66 | Grivory® |
| POLYFORT® FPP 20 GFC LE K1400 | A. Schulman Europe | PP Homopolymer | POLYFORT® |