LNP™ LUBRILOY™ UA200A compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iUE46z_LNPLUBRILOYUA200Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* UA200A is a compound based on Polyphthalamide resin containing Aramid Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound UA-EXP Product reorder name: UA200A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.90 - 1.1 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.4 - 1.6 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.42 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4300 | MPa | ASTM D638 |
| Tensile Strength (Break) | 86.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638 |
| Flexural Modulus | 3720 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.25 | ASTM D3702 Modified | |
| With Self-Static | 0.21 | ASTM D3702 Modified | |
| Wear Factor - Washer | 5.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 254 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 118 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.9E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM E1530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 304 - 316 | °C | |
| Processing (Melt) Temp | 310 - 316 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP692QD | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Axiall PVC 8150 White 209 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| ESPOLEX 487X | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| KOPLA PA66 KDT1030 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| LEXAN™ LUX2289 resin | SABIC Innovative Plastics | PC | LEXAN™ |