VENYL UFRHW 301 NOIR 8229
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iUBfIe_VENYL-UFRHW-301-NOIR-8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VENYL UFRHW 301 NOIR 8229 is a Polyamide 66 (Nylon 66) product filled with 30% glass bead. It can be processed by injection molding and is available in Europe. Applications of VENYL UFRHW 301 NOIR 8229 include automotive and electrical/electronic applications. Primary characteristic: flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.0 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 4100 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 29 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 275 to 290 | °C | |
| Middle Temperature | 270 to 285 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Processing (Melt) Temp | 255 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® B2 BT | Plastcom | PBT | SLOVASTER® |
| ELASTOSIL® R 401/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Haysite SMC 44500 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| HiFill® PA6 0135 BL069 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Hiprolon® 11 ESNNHL P40 | Arkema | Nylon 1012 | Hiprolon® |