TARFLON™ SK2706
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iTwZFk_TARFLON-SK2706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow, Standard |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Spiral Flow | 40.0 | cm | Internal Method |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.40 | % | |
| Flow : 2.00 mm | 0.40 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 50 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 78.0 | °C | ISO 75-2/A |
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 36 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.580 mm | V-1 | ||
| 1.00 mm | V-0 | ||
| 0.800 mm | 5VB |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC+ABS-FR(40)< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ HG20L | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| Xuchuan XCW-9021 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Zhongfa PC/ABS CW-100-FR | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC+ABS | Zhongfa |
| Dynacom 304-G30 | Dynachem Co. Ltd. | Nylon 66 | Dynacom |
| LNP™ COLORCOMP™ MG47C compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |