Eastar™ 6763
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Eastar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iTs23c_Eastar-6763.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eastar™ copolyester 6763 is a clear, amorphous material. Because of its clarity, toughness and good melt strength at processing temperatures, it is useful in a variety of processing techniques including film and sheet extrusion. Eastar™ Copolyester 6763 may be colored using color concentrates, dry colors or liquid colorants. This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®. The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products. This product has been CRADLE TO CRADLE CERTIFIED Silver. The CRADLE TO CRADLE CERTIFIED Mark is a registered certification mark used under license through McDonough Braungart Design Chemistry (MBDC). MBDC is a global sustainability consulting and product certification firm. The CRADLE TO CRADLE® framework moves beyond the traditional goal of reducing the negative impacts of commerce ('eco-efficiency'), to a new paradigm of increasing its positive impacts ('eco-effectiveness'). At its core, Cradle to Cradle design perceives the safe and productive processes of nature's 'biological metabolism' as a model for developing a 'technical metabolism' flow of industrial materials. Product components can be designed for continuous recovery and reutilization as biological and technical nutrients within these metabolisms. For more information about MBDC and to obtain printable certificates for Eastman Copolyesters, visit www.mbdc.com. Choose Eastman Chemical Company under Company Name in C2C Certified products to display a list of our products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.27 | g/cm³ | ASTM D792, ASTM D1505 |
| 23°C | 1.27 | g/cm³ | ISO 1183/D |
| Water Absorption (23°C, 24 hr) | 0.13 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, 23°C | 106 | ASTM D785 | |
| R-Scale, 23°C | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield, 23°C | 50.0 | MPa | |
| Break, 23°C | 28.0 | MPa | |
| Tensile Elongation | |||
| Break, 23°C | 130 | % | ASTM D638 |
| Break, 23°C | 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2100 | MPa | ASTM D790 |
| 23°C | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 68.0 | MPa | ISO 178 |
| Yield, 23°C | 70.0 | MPa | ASTM D790 |
| Tear Resistance | ASTM D2582 | ||
| MD : 23°C, 250.0 µm | 93 | N | |
| TD : 23°C, 250.0 µm | 93 | N |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Permeability (23°C, 250.0 µm) | 49 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Tear Propagation Resistance 1 | ASTM D1938 | ||
| MD : 23°C, 250.0 µm | 36 | kN/m | |
| TD : 23°C, 250.0 µm | 36 | kN/m | |
| Film Thickness - Tested | 250 | µm | |
| Secant Modulus | ASTM D882 | ||
| MD : 250 µm | 1900 | MPa | |
| TD : 250 µm | 1900 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 250 µm | 52.0 | MPa | |
| TD : Yield, 250 µm | 52.0 | MPa | |
| MD : Break, 250 µm | 59.0 | MPa | |
| TD : Break, 250 µm | 55.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 250 µm | 4.0 | % | |
| TD : Yield, 250 µm | 4.0 | % | |
| MD : Break, 250 µm | 400 | % | |
| TD : Break, 250 µm | 400 | % | |
| Dart Drop Impact 2 | ASTM D1709A | ||
| -18°C, 250 µm | 500 | g | |
| 23°C, 250 µm | 400 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 250 µm | 1400 | g | |
| TD : 250 µm | 1700 | g | |
| Trouser Tear Resistance 3 | ISO 6383-1 | ||
| MD | 36.0 | N/mm | |
| TD | 36.0 | N/mm | |
| Oxygen Permeability (23°C, 250 µm, 50% RH) | 10 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 100% RH, 250 µm) | 7.0 | g/m²/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 37 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -40°C | 4.2 | kJ/m² | ISO 180/1A |
| 23°C | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -40°C, 3.20 mm | No Break | ASTM D4218 | |
| -30°C, 3.20 mm | No Break | ASTM D4218 | |
| -20°C, 3.20 mm | No Break | ASTM D4218 | |
| 23°C, 3.20 mm | No Break | ASTM D4218 | |
| -40°C 4 | No Break | ISO 180/1U | |
| -30°C 5 | No Break | ISO 180/1U | |
| -20°C 6 | No Break | ISO 180/1U | |
| 23°C 7 | No Break | ISO 180/1U | |
| Instrumented Dart Impact | |||
| -40°C, 2.50 mm, Energy at Peak Load | 41.0 | J | ASTM D3763 |
| -40°C, 3.20 mm, Energy at Peak Load | 50.0 | J | ASTM D3763 |
| 23°C, 2.50 mm, Energy at Peak Load | 28.0 | J | ASTM D3763 |
| 23°C, 3.20 mm, Energy at Peak Load | 33.0 | J | ASTM D3763 |
| -40°C, 2.50 mm, Energy to Peak Force | 35.0 | J | ISO 6603-2 |
| -40°C, 3.20 mm, Energy to Peak Force | 36.0 | J | ISO 6603-2 |
| 23°C, 2.50 mm, Energy to Peak Force | 40.0 | J | ISO 6603-2 |
| 23°C, 3.20 mm, Energy to Peak Force | 44.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 64.0 | °C | |
| Glass Transition Temperature | 80.0 | °C | DSC |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| CLTE - Flow (-30 to 40°C) | 5.1E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | DSC | ||
| 60°C | 1300 | J/kg/°C | |
| 100°C | 1760 | J/kg/°C | |
| 150°C | 1880 | J/kg/°C | |
| 200°C | 1970 | J/kg/°C | |
| 250°C | 2050 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.21 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 8(23°C) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 23°C, 1 kHz | 2.60 | ||
| 23°C, 1 MHz | 2.40 | ||
| Dissipation Factor | ASTM D150 | ||
| 23°C, 1 kHz | 5.0E-3 | ||
| 23°C, 1 MHz | 0.020 | ||
| Arc Resistance | 158 | sec | ASTM D495 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 250 µm) | 108 | ASTM D2457 | |
| Transmittance | ASTM D1003 | ||
| Total, 250 µm | 91.0 | % | |
| Regular, 250 µm | 89.0 | % | |
| Clarity (250 µm) | 85.0 | ASTM D1746 | |
| Haze (250 µm) | 0.80 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Split Tear Method, 254 mm/min |
| 2 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 3 . | 200 mm/min |
| 4 . | 4 mm |
| 5 . | 4 mm |
| 6 . | 4 mm |
| 7 . | 4 mm |
| 8 . | 500 V/sec, Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| E-FLEX™ S4060 | Mando Advanced Materials Co., Ltd. | TPE | E-FLEX™ |
| KPOL-NYLON K-NY66/21VCF | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| OmniTech™ ABS GR10 | OMNI Plastics, LLC | ABS | OmniTech™ |
| Petrothene® LR763011 | LyondellBasell Industries | HDPE | Petrothene® |
| ALTECH® PC ECO 1000/141 FR IM | ALBIS PLASTIC GmbH | PC | ALTECH® PC |