RTP 1390
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iSaz10_RTP-1390.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 46200 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 98.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 38600 | MPa | ASTM D790 |
| Flexural Strength | 221 | MPa | ASTM D790 |
| Compressive Strength | 190 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 130 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 260 | °C | ASTM D648 |
| CLTE - Flow | 1.3E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.61 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 1mil/in.The value listed as flammability, UL 94, was tested in accordance with RTP test standards.RTP 1380 Series materials are carbon fiber polyphenylene sulfide materials. They are characterized by excellent physical properties, high moduli, heat resistance and are inherently flame retardant. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 285 - 343 | °C | |
| Middle Temperature | 285 - 343 | °C | |
| Front Temperature | 285 - 343 | °C | |
| Mold Temperature | 65.6 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 60 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tygon R-3400 | Saint Gobain - Norton | PVC, Unspecified | Tygon |
| Hifax RTA3263UV | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Jackdaw PP ER14BK8003 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| LIM™ 6040 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | LIM™ |
| POCAN® ECO T 3240 000000 | LANXESS Corporation | PBT+PET | POCAN® |