Order Products : sales@su-jiao.com
Ecodear® V554X51
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Toray Resin Company |
| Trademark: | Ecodear® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iRatMS_Ecodear-V554X51.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ecodear® V554X51 is a Polylactic Acid (PLA) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.27 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 78.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5V |
| Note Message | |
|---|---|
| 1 . | Sink-float Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sekisui PVC TG-40 | Sekisui (Hong Kong) Limited | PVC, Unspecified | Sekisui PVC |
| Andur RT 9002 AP | Anderson Development Company | PUR-TDI | Andur |
| Durez® 7716 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| 3M™ Dyneon™ Fluoroelastomer FX 9194 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| CERTENE™ PBM-20 | Muehlstein | PP Impact Copolymer | CERTENE™ |