Romiloy® 2720
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iQmZEq_Romiloy-2720.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®2720 is a polycarbonate PET (PC PET) material,. This product is available in Europe, and the processing method is injection molding. Romiloy®The main features of the 2720 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2340 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 92.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 750 | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901.Tensile Strain at Break, ISO 527, 23°C, 50 mm/min: >100% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 260 - 290 | °C | |
| Middle Temperature | 260 - 290 | °C | |
| Front Temperature | 260 - 290 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | < 1.00 | MPa | |
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Holding Pressure: moderate to high |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT1001-00 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Tecnoprene® AK7HCT NAT001 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| Nipol® BR 1220 | Zeon Corporation | PBR, High Cis | Nipol® BR |
| Daelim Po1y® TR-420 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| PENTAMID A GV15 MA15 H RC schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |